Project Management and Feasibility Studies for Iron and Steel Industry | ESR Flux, Cored Wire

Optimize Steel Production with Cored Wire and Copper Tube

CaSi CORED WIRE;

Ca:28-32%, Si：58-62%， Al:2%max, C:1.0%max

Dia: 13mm+/-0.5mm Thickness:0.4+/-0.05mm

Filling rate:230+/-10g/m,1135kg/coil+/-10%

Steel weight:165+/-10g/m,765kg/coil+/-10%

Wire weight:395+/-10g/m,1900kg/coil+/-10%

Wire length: 4935m+/-10% Coil ID: 600mm Coil OD: 1100mm Height: 1100mm

CaFe CORED WIRE

Ca:28-32%, Fe:68-72%

Dia: 13mm+/-0.5mm

Thickness:0.4+/-0.05mm

Filling rate:260+/-10g/m,1250kg/coil+/-10%

Steel weight:165+/-10g/m,750kg/coil+/-10%

Wire weight:425+/-10g/m,2000kg/coil+/-10%

Wire length: 4820m+/-10%

Coil ID: 600mm Coil OD: 1100mm Height: 1100mm

PURE Ca CORED WIRE

Ca:98.5%min

Dia: 9mm+/-0.5mm

Thickness:0.5+/-0.05mm

Filling rate: 70+/-5g/m

Wire weight:2000kg/coil+/-10%

Wire length: 9090m+/-10%

Coil ID: 600mm Coil OD: 1100mm Height: 1100

ESR FLUX

Quality, not quantity

Slag has an important role in controlling inclusions in the ESR process. The chemical and physical properties of slag also have a great impact on the removal of inclusions.

Slag Maker for Seconder Metallurgy

Sintered Calsium Aluminate

Pre-Fused Calsium Aluminate

Silica Based Synthetic slag maker

Calsium Fluoride

WATER COOLED COPPER CABLE FOR EAF&LF

GRAPHITE ELECTRODE FOR EAF&LF

The Graphite electrodes are produced through calcined material under high pressure in vacuum impregnation and then Graphitized at Graphitization Furnace; finally they are machined.The electrodes are supplied 100-700mm diameter with specification RP(Regular Power), HP and UHP.
High Power grade is for foundry operations, for the ladle furnace and occasionally for the electric arc furnace operations, if the furnace parameters are suitable. Ultra High Power grade is suitable for the electric arc furnace (EAF) operations and the ladle furnace operations with heavy current loads.